Results of XRD indicated that CexPd1-xO2-δ solid solution was formed when the catalysts were calcined at 400-800 ℃,while PdO or metal Pd species re-migrated to the catalyst surface when it was calcined at a higher temperature(1000 ℃).
XRD结果表明,焙烧温度从400℃升高到800℃,有利于CexPd1-xO2-δ固溶体的形成。
XRD results indicated that a Ce_xPd_(1-x)O_(2-δ) solid solution was formed when the catalysts were calcined at 400-800℃,while PdO or metal Pd species re-migrated to the catalyst surface when it was calcined at a higher temperature(1000℃).
XRD实验结果表明,焙烧温度从400℃升高到800℃,有利于催化剂中Ce_xPd_(1-x)O_(2-δ)固溶体的形成,然而焙烧温度升至1000℃时,导致Pd物种从固溶体中析出。
-
problem of geometrical constru
精品项目网为您提供几何准问题problem of geometrical construction是什么意思,problem of geometrical construction翻译,problem of geometrical construction例句,problem of geometrical construction用法等有关,problem of geometrical construction单词...
-
fundamental interactions
精品项目网为您提供基本相互作用fundamental interactions是什么意思,fundamental interactions翻译,fundamental interactions例句,fundamental interactions用法等有关,fundamental interactions单词知识大全供您查询使用!...